简介：TheDCcharacteristicsofSiGeHBTirradiatedatdifferentelectrondosehavebeenstudiedinacomparisonwiththoseofSiBJT.Generally,IbandIb-Ib0increase,Ic,Ic-Ic0andits+/-transitionVbeaswellasDCcurrentgainβdecreaseswithincreasingdose;increaseofIb-Ib0withincreasingdoseforSiBJTismuchlargerthanthatforSiGeHBT;βincreaseswithVbeorIb,butdecreasesatIb＜0.25mAwithIb,andcongregatesathigherdose;andadamagefactord(β)ismuchlessatthesamedoseforSiGeHBTthanforSiBJT.SiGeHBThasmuchbetteranti-radiationperformancethanSiBJT.SomeanomalousphenomenaforincreaseofIc,Ic-Ic0,Ib-Ib0andβatlowdosehavebeenfound.Someelectrontrapshavebeenmeasured.Themechanismofchangesofcharacteristicsisdiscussed.

简介：

简介：采用SEM、TEM、EDS、DSC、XRD和拉伸实验研究铸态7X50合金及其均匀化处理过程的组织演变。结果表明,铸态7X50合金相组成主要有S(Al2CuMg)、T(Al2Mg3Zn3)、MgZn2和少量的Al7Cu2Fe和Al3Zr相。均匀化处理过程中枝晶网和残留相逐渐减少,经(470°C,24h)+(482°C,12h)均匀化处理时,T相消失,S相有微量残留,Al7Cu2Fe相几乎没有变化。铸态合金的DSC曲线中在477.8°C处有一较强吸热峰,经470°C、1h均匀化后合金的DSC曲线在487.5°C处出现一个新的吸热峰,而经482°C、24h均匀化处理后合金在487.5°C处的吸热峰基本消失。在XRD谱中未出现T(Al2Mg3Zn3)相,这和T相与S(Al2CuMg)及MgZn2相相关的结论相吻合。预均匀化处理制备的板材中再结晶晶粒分数明显降低,抗拉强度和断裂韧性相对常规均匀化处理制备的板材分别提高约15MPa和3.3MPa·m1/2。

简介：为实现飞机碳纤维复合材料(CarbonFiberReinforcedPlastics,CFRP)层板在役检测,采用同侧空气耦合超声兰姆波特征成像检测的方法对其缺陷进行检测。将非接触空气耦合超声传感器置于CFRP层板同侧,激发A0模态兰姆波,对其冲击损伤进行D扫描检测。引入时间反转损伤指数表征复合材料层板的冲击损伤。结合概率损伤算法,以该指数作为损伤重构成像的特征值,将不同扫描路径上的特征值数据进行融合,得到CFRP层板冲击损伤缺陷的兰姆波图像。结果表明,基于时间反转的兰姆波图像不仅能够直观地呈现损伤缺陷的位置和形状,而且能够通过避免基准信号选取和减少扫描步进次数显著提高检测效率。