简介:Vibrationfatigueisthemainfailuremodeofcompressorblade.Evaluatingthevibrationstressofbladethatleadstocrackingisveryusefulforanalysisofvibrationfatigue.Inthispaper,fatiguestressestimationmethodsbyquantitativefractographywerestudiedthroughexperimentalbladeandin-servicefirst-stagecompressorbladeinordertoevaluatetheinitiationvibrationstressofin-serviceblade.Theanalysisprocessofinitiationvibrationstresswasestablished.Theevaluatingresultofvibrationstressofin-servicebladesubjectedtocentrifugalforceandbendingvibrationstressagreeswithaeroenginetestresult.Itisshownthattheevaluationmethodcannotonlyevaluatetheequivalentfatiguestressesofdifferentcrackdepthsbutalsoyieldtheinitiationequivalentfatiguestress.
简介:钛及其合金常被用作牙科和骨植入材料。钛表面的仿生涂层可以改善其成骨性能。本文作者开发一种新型的、具有成骨作用的钛合金表面纳米复合涂层,为骨髓间充质干细胞(MSCs)的粘附、增殖和成骨分化提供自然环境。用静电纺丝法制备基于聚己内脂(PCL)、纳米羟基磷灰石(nHAp)和雷尼酸锶(SrRan)的纳米复合涂层。因此,涂覆在钛合金表面的涂层有4种,分别为PCL、PCL/nHAp、PCL/SrRan和PCL/nHAp/SrRan。采用EDS、FTIR、XRD、XRF、SEM、AFM、体外细胞毒性和血液相容性测试等技术评估涂层的化学性能、形貌和生物学性能。结果表明,纳米复合涂层具有细胞相容性和血液相容性,PCL/HAp/SrRan纳米复合纤维涂层具有最高的细胞活性。MSCs在纳米涂层上的成骨培养显示干细胞向成骨分化,碱性磷酸酶活性和矿化测试结果证实了这一点。研究结果表明,所制备的复合纳米涂层具有促进新骨形成和增强骨-植入体整合的潜力。
简介:日前山东招金集团第三届科技大会召开,为落实大会工作部署,全力推动山东招金集团科技创新工作,围绕行业共性技术难题、企业发展科技攻关重点以及未来公司发展的前瞻性课题研究,经公司山东招金集团研究,确定了十一项重点攻关课题,作为未来三年公司科技创新的主攻方向。十一项重点攻关课题(攻关课题的主要方向与内容)如下:l、招平断裂带中部成矿研究(课题来源:招金矿业股份有限公司);2、金矿深部通风、降温、地压管理研究(课题来源:招金矿业股份有限公司夏甸金矿);3、快速成井、成巷施工技术研究与应用(课题来源:招金矿业股份有限公司夏甸金矿);4、非爆采掘技术研究(课题来源:招金矿业股份有限公司早子沟金矿);5、非化学(含无氰)选冶技术研究(课题来源:招金矿业股份有限公司技术中心);6、采、运自动化技术研究与应用(课题来源:招金铜完成7020吨,超计划520吨。技术指标方面,一月份精锌单耗粗锌、精铅单耗粗铅对比2014年12月份均略有下降,矿产铟回收率对比上月提高4.84%,精锌厂镉回收率对比去年提高了1.69%,;综合利用厂碱渣铟精炼回收率完成90.8%,对比去年同期提高了0.59%;电解锌厂锌总回收率完成97.63%,同比提高了0.43%;铟渣回收率完成55.95%,同比提高了15.95%。(新闻来源:中冶葫芦岛有色金属集团有限公司)
简介:激光粉末免职被使用制作Ti-6.5Al-3.5Mo-1.5Zr-0.3Si(wt%)/Ti-47Al-2Cr-2Nb-0.2W-0.15B(at%)双性人材料系统。当同样扔的-TiAl合金由组成时,同样扔的TC11合金显示出basket-wave-like形态学充分2/薄片状的微观结构。在处理期间考虑在TC11和-TiAl之间的热失配,接口微观结构进化被担心。转变小径被说明。艾尔元素和-stabilizers瞬间,Cr,和Nb的内容变化为在接口的微观结构的进化负责,这被发现。破裂表面在-TiAl方面被定位。双性人材料显示出一种易碎破裂的方式,与560的最终的张力的力量?MPa。
简介:TheslidingfrictionandwearbehaviorsofMg–11Y–5Gd–2Zn–0.5Zr(wt%)alloywereinvestigatedunderoillubricantconditionbypin-on-diskconfigurationwithaconstantslidingdistanceof1,000minthetemperaturerangeof25–200°C.Resultsindicatethatthevolumetricwearratesandaveragefrictioncoefficientsdecreasewiththeincreaseofslidingspeeds,andincreasewiththeincreaseoftesttemperaturebelow150°C.ThehardandthermallystableMg12(Y,Gd)Znphasewithlong-periodstackingorderstructureinthealloypresentssignificantwearresistance.Thewearmechanismbelow100°Cisabrasivewearasaresultofplasticextrusiondeformation.Thecorporateeffectsofsevereabrasive,oxidative,anddelaminatingwearresultinthetribologicalmechanismabove100°C.
简介:研究纳米羟基磷灰石(HAP)涂覆的多孔Mg-2Zn(质量分数,%)支架材料的生物降解能力和生物相容性。采用脉冲电沉积制备羟基磷灰石涂层。对涂覆HAP的支架在碱性溶液中进行后处理来改善其生物降解性和生物相容性。研究支架和HAP涂层的显微组织和成分以及它们在模拟体液(SBF)中的降解和细胞毒性。经过碱溶液处理后的涂层由几乎垂直于基体的直径小于100nm的针状HAP组成,具有和天然骨头相似的成分,浸泡在SBF中后,产物为HAP、(Ca,Mg)3(PO4)2和Mg(OH)2。涂覆HAP和经过处理碱处理后的支架比未涂覆HAP的支架具有更高的生物相容性和细胞存活性。MG63细胞粘附在涂覆HAP和经过碱处理后的支架的表面并增殖,使这些支架有望应用于医学。结果表明:纳米HAP的脉冲电沉积和碱处理可有效改善多孔Mg-Zn支架的生物降解能力和生物相容性。
简介:激光冲击强化是一种新型表面处理技术,利用高功率激光束冲击金属零件表面,在零件表面形成较大的残余压应力,可有效改善零件的疲劳性能。以发动机1Cr11Ni2W2MoV叶片为研究对象,对其进行了激光冲击强化处理,研究强化处理对材料的微观组织和疲劳性能的影响。研究结果表明:相比未处理试样,激光冲击强化在1Cr11Ni2W2MoV叶片材料表层形成较大的残余压应力,表层晶粒更为细化,叶片的疲劳寿命提高1.7倍。