ThesubmicronpowdermixturesofTiC-TiN-WC-Mo-C-Nisinteredat1400℃orbelowinvacuumwerestudiedbyX-raydiffraction(XRD),scanningelectronmicroscopy(SEM)andtransmissionelectronmicroscopy(TEM)analyses.TheresultsshowedthatMo2Cformedat800℃orbelow.BothWCandMo2Cdisappearedat1200℃,andTiNdisappearedat1250℃.Inaddition,thevariationsoflatticeconstantsofthetitaniumcarbonitrideandnickelbinderphasewithsinteringtemperaturewereexperimentallyobtained,andthereasonwasanalyzed.