Recrystallization behavior of twin roll cast low carbon steel strip-中国期刊网

摘要 Thedynamicandstaticrecrystallizationbehaviorsoftwinrollcastlowcarbonsteelstripwereinvestigatedwithanattempttoprovideguidingdeformationparametersfortheonlinehotrolling.Inordertoinvestigatedynamicrecrystallizationbehavior,ascaststripwasreheatedandsoakedwithaustenitegrainsizesimilartothewidthleveloftheascastcolumnarstructure.Tensiletestwasusedandthedeformationtemperatureisintherangeof900℃to1100℃andstrainratesare0.01s-1,0.1s-1,1s-1.Theactivationenergyandstressexponentweredeterminedas306kJ/moland4.69respectively.Theratioofcriticalstraintothepeakstrainis0.65,andthatofcriticalstresstothepeakstressis0.92.ThedependenceofthepeakstrainontheinitialgrainsizeandZener-HollomonparametersZisεp=9.1×10-4×D00.48Z0.13.Thekineticsofthedynamicrecrystallizationandrecrystallizedgrainsizewaspredictedusingmodelspublished.Theascastcoarseausteniteweredramaticallyrefinedaftercompletedynamicrecrystallization.Forstaticrecrystallization,thetensiletestwascarriedoutonGleeble-3500thermo-mechanicalsimulator.Thedeformationtemperatureisintherangeof800℃to1200℃withstrainrate0.01s-1to1s-1.Theprestrainisfixedat0.04to0.12andtheinter-hitdelaytimevariesfrom1sto3000s.TheactivationenergyandAvramiexponentofstaticrecrystallizationweredeterminedas241kJ/moland0.54respectively.Akineticsmodelwasproposedtodescribethestaticrecrystallizationkinetics.Thepredictedresultswereingoodagreementwiththeexperimentalresults.

1FANG Yuan,CUI Jian,YU Yan,WU Jianchun and WANG Chenquan Baoshan Iron & Steel Co.,Ltd.,Shanghai 201900,China. The key technologies of controlling low carbon steel as-cast strip surface quality.钢铁冶金,2010-04.
2YE Changhong;FANG Yuan;ZHANG Qing. Study of measurement and control of free loop of hot steel strip in twin-roll strip casting.钢铁冶金,2018-01.
3WANG Jian;LI Jun;ZHANG Lixiang;XIE Yingxiu. Effect of heating rate on the recrystallization microstructure and property of ultra-low-carbon steel.钢铁冶金,2014-01.
4Na LI Zhenyu LIU Yiqing QIU Zhaosen LIN Xianghua LIU Guodong WANG. Solidification Structure of Low Carbon Steel Strips with Different Phosphorus Contents Produced by Strip Casting.材料科学与工程,2006-06.
5ZHENG Hongguang;SHEN Jicheng;WU Difeng;SUN Dan;CHEN Weiqing. Effect of Ti and Nb on the recrystallization of ultra low carbon and nitrogen Cr18 stainless steel.钢铁冶金,2010-01.
6YANG Feng;SU Daxiong;ZHANG Wenlong. Influence of cold forming on the tensile behavior and properties of low-carbon microalloyed steel.钢铁冶金,2010-03.
7ZHANG Weidong~(1)),ZHANG Jieyu~(1)),WANG Bo~(1,2)),REN Sanbing~(3)), FAN Junfei~(3)),FANG Yuan~(3)) and YU Yan~(3)) 1) School of Material Science and Engineering,Shanghai University,Shanghai 200072,China 2) Material and Metallurgical School,Inner Mongolia University of Science and Technology,Baotou 014010,China 3) Research Institute,Baoshan Iron and Steel Co.,Ltd.,Shanghai,201900,China. Mathematical modeling of fluid flow and level profile during twin-roll strip casting process.钢铁冶金,2010-08.
8谌岩. Layer Structure Analysis of Low-Carbon Steel Containing Rare Earth by High-Temperature Carburizing of Liquid Cast-Iron.有色金属冶金,2004-05.
9BAO Yanping,WANG Min,CUI Heng,WU Weishuang and WU Huajie School of Metallurgical and Ecological Engineering,University of Science and Technology Beijing,Beijing 100083,China. Evolution of inclusions in Ti stabilized ultra low carbon steel(Ti-IF) steel.钢铁冶金,2010-04.
10WEN Hongquan;QIN Xiaofeng;WU Qiong. Rolling-contact-fatigue behavior in backup roll of 5 % Cr forged steel.钢铁冶金,2018-01.

Recrystallization behavior of twin roll cast low carbon steel strip

来源期刊

相关推荐

同分类资源更多

相关关键词

Recrystallization behavior of twin roll cast low carbon steel strip

来源期刊

相关推荐

同分类资源 更多

相关关键词

同分类资源更多