简介:TheNaYF4:Yb,Ernanocrystalsweresynthesizedviathethermaldecompositionofmetaloleateprecursors.Thenanocrystalsinhexagonalstructurewerehighlyuniformandinsizeof25nm.Thebrightupconversionluminescencewasobservedundertheexcitationof980nmlaserandtheupconversionemissionspectrawereinvestigatedatdifferentpumppowers.Theemissionintensityratioofredlighttogreenlightlinearlyincreasedwithpumppowerincreasing.ThisresultindicatedthatthereexistedalargethresholdpowerofsaturationpumpforthefirstexcitationstateinNaYF4:Yb,Ernanocrystalscomparingtothatinbulkmaterial.
简介:Resinsofcomplexesmadefromagarose-Ce4+(RCA-Ce)andchitosan-Ce4+(RCC-Ce)wereprepared.Hydrolysisratesofmethamidophos,omethoateandchlorpyrifostreatedbyRCA-Cewere32.39%,27.12%and46.62%,respectively,thoseofchlorpyrifosandmethamidophosinmungbeansproutjuice38.28%and35.45%,andthatofchlorpyrifosinteaextract59.76%.HydrolysisratesofproteininteaextracttreatedbyRCA-Ceincreasedby86.46%.RCC-Cecouldbeemployedintheapplejuiceproduction.Thecontentsofmethamidophosandparathion-methylinthejuicetreatedbyRCC-Cedecreased58.76%and71.92%.Furthermore,RCC-Cewasusedtoclarificationforbeerbythewaysofacolumn.RCC-Cecouldhydrolyzesensitiveproteinandincreasecontentsoffreeaminoacidinthebeer.Therefore,thebeertreatedbyRCC-CecouldstayoxidationandagingprocedureduetosomemetalionsbeingabsorbedbyRCC-Ce.
简介:YbAl3(BO3)4crystalofgoodopticalqualitywasgrownbythefluxmethod.ThestructureofYbAl3(BO3)4crystalwasdeterminedbysingle-crystalX-raydiffraction.TheexperimentshowsthatYbAl3(BO3)4belongstothedoubleborateswithatrigonalstructure.ThespacegroupisR32anditsunitcellconstantsweremeasuredtobea=0.92965nm,c=0.72129nm,V=0.53673nm3,Z=3.Thetransmittancespectraweremeasured.Thecut-offofYbAl3(BO3)4crystalis216nm,andtherearetwoabsorptionpeakslocatedat940and975nmfrom190nmto2600nm.ThethermalpropertiesofYbAl3(BO3)4crystalwerestudiedforthefirsttime.Theaveragethermalexpansioncoefficientsweredeterminedtobe2×10-6/℃,9.5×10-6/℃alonga-andc-direction.ThespecificheatofYbAl3(BO3)4crystalwasmeasuredtobe0.6695J·(g·℃)-1atroomtemperature.AllresultsindicatethattheYbAl3(BO3)4crystalisanexcellentstoichioimetriclasermaterial.
简介:Thesynthesisofprecursorofgreenphosphors,LaPO4:Ce,Tb,bymeansofco-precipitationwithcocurrentflowfeedwasstudied.Theeffectsofthereactiontemperature,thekindandconcentrationoftheacidinthebottomwater,andthechargingrateonthephysicalproperties,suchasparticlesize,wereinvestigated.Itisfoundthattheparticlesizeofthepowderiscontrollablebyadjustingacidityinbottomwaterandchargingrate.Thepowderwithdiametersizeof3to5μmwasobtained.ItsXRDandSEMwereanalyzed.XRDpatternsoftheas-preparedgreenphosphorpowdersdisplaythetypicalpeaksofCePO4.SEMshowsthatthemorphologyofpowdersisball-shaped.
简介:对退火态AHPT15M粉末高速钢进行盐浴淬火处理,然后对退火态样品与淬火态样品进行深冷处理、回火处理和同步热磁分析,研究深冷处理对AHPT15M粉末高速钢回火转变的影响。结果表明,退火态粉末高速钢中的铁素体含量(体积分数)约为71.5%;淬火态钢中的马氏体含量(体积分数,下同)约为45.2%,在经过1、2、3次823K/1h连续回火处理后,马氏体含量分别约为68.5%、71.0%和71.3%;回火前增加143K深冷处理工序,在深冷后和l、2、3次回火后,钢中马氏体含量分别约为59.8%、69.9%、70.9%和71.3%。深冷处理可提前残留奥氏体向马氏体的转变进程、抑制残留奥氏体中的碳化物析出,并促进马氏体中更大量(约2.3%)的微细碳化物析出,使钢的硬度提高52HV0.1。