简介：PolycrystallinesamplesofLa12x(Sr12yAgy)xMnO3(y=0.0,0.2,0.4,0.6,1.0)werepreparedbythesolid-statereactionmethod.ThetemperaturestabilityofmagnetoresistanceandmagnetoresistanceenhancementinLa1-x(Sr1-yAgy)xMnO3systemwithbothunivalentandbivalentelementsdopedatAsiteandwithunchangedvalueofMn3+/Mn4+ratiowereexploredthroughthemeasurementsofX-raydiffractionpatterns,magnetiza-tion-temperature(M-T)curves,resistivity-temperature(q-T)curvesandmagnetoresistance-temperature(MR-T)curves.Theresultsareasfollows:therearetwopeaksintheq-TcurvesofthesampleswithAgdoping,oneiscausedbyresistancechangeduringtheparamagnetism-ferromagnetismtransition,andtheotherisfromboundary-dependentscatteringofconductionelectronsontheboundariesofgrains.ThepeakvalueofMRincreaseswithincreasingAgdopingcontent,anditincreasesfrom8.2%fory=0.2to29.6%fory=1.0underthemagneticfieldofB=0.8T;MRremainsaconstantof12%inthetemperaturerangeof218-168Kforthesamplewithy=1.0,andthetemperaturestabilityofMRisinfavorofthepracticalapplicationofMR.

简介：有不同Y_2O_3内容的基于钴的合金被扔用血浆的onQ235A碳钢转移了焊接机器的弧(PTA)。微观结构上的Y_2O_3的效果并且穿基于钴的合金的抵抗性质用一台光显微镜，一台扫描电子显微镜(SEM)，X光检查衍射(XRD)，和传播电子被调查显微镜学(TEM)。有face-centeredcubic晶体结构的一个基于钴的稳固的答案被介绍，这被发现在Y_2O_3免费的基于钴的合金涂层与六角形的晶体结构由第二等的阶段M_7C_3伴随了。几叠差错在基于钴的稳固的答案存在。Y_2O_3的增加在修改Y_2O_3的涂层导致Y_2O_3阶段的存在。尽管叠差错在修改Y_2O_3的涂层存在，它的密度增加。Y_2O_3的增加能精制微观结构并且当它的内容小于等于0.8wt.%时，能增加wear抵抗性质。然而，它的内容的另外的增加将在γ-Cograin边界导致undissolvedY_2O_3粒子的凝块，并且将导致粗糙的微观结构并且降低穿抵抗性质。

简介：pH价值和Y2Y23-SiO2(Y-Si)泥浆>为Ti-6Al-4V投资扔的脸上衣的O3粉末和硅石大音阶的第五音被测量。Y-Si脸上衣系统做的壳的热行为被微分扫描热量计(DSC)调查，热gravimetric(TG)分析与集体spectrometry(MS)结合了，并且阶段转变被X光检查衍射(XRD)决定。热力量，剩余力量，线性扩大系数，和壳的穿的抵抗性能也被测试。微观结构和相互作用层的元素分发被分别地扫描电子显微镜(SEM)和精力散的分光计(版本)学习。microhardness测试者被申请microhardness。结果证明泥浆为至少60是稳定的?h。YZrO3的很小的数量低于1050被形成?普牯慭?楦汥?桴潥祲?畢?畯?敲?瑬?灡汰?畱污瑩瑡癩汥?潴愠眠摩牥挠慬獳漠?睴?楤敭獮潩慮?楤慬潴?牧癡瑩?桴潥楲獥?潆?慥档琠灹?景猠汯瑵潩獮眠?数晲牯?潨潬牧灡楨?敲潮浲污穩瑡潩?挠浯異吗？？

简介：采用磁控溅射法成功制备Al2O3/Au层状复合纳米涂层,所制备的涂层结构致密且由Al2O3层和Au层交替组成。采用高温循环氧化实验对复合涂层在不锈钢基体上的高温抗氧化性能进行分析评价。结果表明：Al2O3/Au层状复合纳米涂层极大地改善不锈钢基体的抗氧化和抗剥落性能。其抗氧化机理与涂层能够有效地抑制氧向合金基体的扩散并促进不锈钢基体中Cr元素的选择性氧化有关;抗剥落机理可归因于复合涂层中的Au层和纳米结构的Al2O3层能够有效地松弛高温热循环过程中产生的热应力,从而提高涂层的抗剥落性能。

简介：通过水热法成功合成Co3O4/CuO复合物,并探索十六烷基三甲基溴化铵(CTAB)和聚乙烯吡咯烷酮(PVP)对其形貌和性能的影响。用X射线衍射仪(XRD)、扫描电子显微镜(SEM)、透射电子显微镜(TEM)和氮气吸附-脱附测试表征其微观结构和表面形貌。采用循环伏安、恒流充放电和交流阻抗测试等方法研究样品的电化学性能。结果表明,多孔Co3O4/CuO-CTAB纳米片具有最好的电化学性能,在电流密度1A/g下的比容量达398F/g,而在10A/g时其比容量仍能保持90%。此外,该复合物具有很好的循环稳定性,在2000次循环后容量几乎没有衰减。

简介：Twinninganddetwinningaretheimportantdeformationmodesinmagnesiumalloysduringcyclicloadingatroomtemperature.Toanalyzethesetwodeformationmechanism,cycliccompression–tensionexperimentswereperformedonMg–3Al–1Znrolledsheetalongtherollingdirection.Inthesetests,themicrostructureevolutionsofaseriesofgrainsduringdeformationweretracedbyusingquasiinsituelectronbackscatterdiffraction(EBSD).ImportantquantitiesliketheSchmidfactorsoftwinningsystem,thefractionoftwinningduringcompression,andthefractionoftwinningafterreverseloadingwerecalculatedonthebasisofmeasuredquantities.TheinfluenceofSchmidfactoroftwinningvariantsondetwinninguponreverseloadingwasanalyzed.DetwinningwouldprefertoproceedduringreverseloadingiftheSchmidfactoroftwinninginthetwinningareabeforereverseloadingissufficientlylarge.

简介：TheeffectofAl-3Ti-0.2C-5Sr(wt%)grainrefinerontherefiningperformanceandmodificationofA356alloywasinvestigatedusingopticalmicroscope(OM).ThemorphologyandcrystalstructureofternaryAl-Ti-SrphasesinAl-3Ti-0.2C-5Srrefinerwereanalyzedbyscanningelectronmicroscopy(SEM)andtransmissionelectronmicroscopy(TEM).TheresultsshowthattheternaryAl-TiSrphasesinAl-3Ti-0.2C-5SrrefinercanpromotethegrainrefiningefficiencyofA356alloy.TheternaryAl-Ti-Srphasesco-existintwomorphologies,i.e.,blocky-likephaseandsurround-likephase,besides,whichbothhavethesamechemicalcompositionofAl_(34)Ti_3Sr.ThecrystalstructureofAl_(34)Ti_3Srisface-centeredcubic,andthelatticeparameterisdeterminedtobeabout1.52nm.

简介：Li1.3Al0.3Ti1.7(PO4)3pelletssinteredwithdifferentmolefractionsofLiBO2werepreparedbysol-gelmethod.Thestructuralidentification,surfacemorphology,ionicconductivity,andactivationenergyofthepelletswerestudiedbyX-raydiffraction,scanningelectronmicroscopy,andelectrochemicalimpedancespectroscopy.TheresultsshowthatalltheLi1.3Al0.3Ti1.7(PO4)3pelletssinteredwithdifferentmolefractionsofLiBO2havesimilarX-raydiffractionpatterns.ThesinteredpelletbecomesdenserandtheboundaryandcorneroftheparticlesbecomeillegiblewiththeincreaseofLiBO2.AmongtheLi1.3Al0.3Ti1.7(PO3)4pelletssinteredwithdifferentmolefractionsofLiBO2,theonesinteredwith1mol%LiBO2showsthehighestionicconductivityof3.95×10-4S.cm-1andthelowestactivationenergyof0.2469eV.

简介：钛酸铝系复合材料中钛酸铝的体积分数不同，会导致Al2TiO5／Al2O3复合材料的抗铝液浸渗性能的不同。在Al2TiO5中分别按10％、20％、40％、60％、80％、90％（体积分数）引入Al2O3进行复合。通过对渗铝试样的外观形貌、微观结构分析，进而对其铝液浸渗性能进行了分析比较，发现富钛酸铝的钛酸铝／氧化铝复合材料（妒（AL2TiO5）〉40％）抗铝液浸渗性能好；而富氧化铝的钛酸铝／氧化铝复合材料（φ（Al2TiO5）〈20％）有金属铝液沿热震产生的裂纹渗入复合材料内部，容易导致复合材料断裂失效。该研究结果对可靠应用钛酸铝系复合材料作为铝液的容器具有实际工程应用价值。

简介：基于炉渣结构分子和离子共存理论,建立1273-1733K下的PbO-CaO-SiO2-FeO-Fe2O3渣系氧化铅活度热力学模型,计算PbO活度并绘制等活度曲线,考察炉渣碱度Q、氧化铁比率R和温度T对活度NPbO和活度系数γPbO的影响。结果表明,活度系数γPbO的模型计算值与文献测定值吻合程度高,说明该模型能较好地反映该渣系结构本质;NPbO呈拉乌尔正偏差,且随渣中PbO含量的升高而增大,但受温度的影响不明显;γPbO随Q的升高而增大;对于Q〉0.3的碱性渣,γPbO随R的升高而出现极大值。该研究结果可用于现代炼铅工艺的热力学研究和操作优化。

简介：在823K和973K的条件下,采用恒电流密度共电沉积法在LiCl-KCl-MgCl2-Gd2O3熔盐体系中制备Mg-Li-Gd合金,并运用XRD、SEM、EDS和OM对所制备合金进行微观组织分析。结果表明:在开始的30min内,主要是Mg和Gd的沉积,所得合金含96.53%Mg,3.20%Gd和0.27%Li(质量分数),然后Li迅速沉积。可以通过控制电解时间或改变Gd2O3的浓度调节Mg-Li-Gd合金的组成。XRD分析可知,在Mg-Li-Gd合金中存在Mg3Gd相和Mg2Gd相。从Gd元素的面扫描分析可知,Gd元素主要分布在Mg-Li-Gd合金的晶界处。Gd的添加增强了合金的抗腐蚀能力。

简介：中国人民银行定于2010年3月23日发行中国古典文学名著——《水浒传》彩色金银纪念币（第2组）一套。该套纪念币共5枚，其中金币2枚，银币3枚，均为中华人民共和国法定货币。该套纪念币发行规格为1／3盎司彩色圆形金质纪念币，最大发行量为35000枚；5盎司彩色长方形金质纪念币，最大发行量为900枚；1盎司彩色圆形银质纪念币（2枚），最大发行量各为70000枚；5盎司彩色长方形银质纪念币，最大发行量为12000枚。

简介：1Cr15Ni4Mo3N沉淀硬化不锈钢螺栓零件在制造工序磁粉检测时，发现螺栓表面有一条疑似裂纹状线性磁痕显示，后采用荧光渗透检测方法进行辅助检测，原磁痕显示处未见异常荧光显示。结合金相试验分析发现，螺栓原材料内呈带状分布的残余奥氏体，破坏了基体组织和材料磁性的连续性导致出现磁痕显示。研究为该材料在零件制造中磁粉检测的磁痕判定提供了依据。

简介：针对23Co14Ni12Cr3Mo超高强度钢材料,研究喷丸强化对其表面性能的影响。采用扫描电镜、白光干涉仪等设备,分析喷丸强化对试样表面形貌、粗糙度、硬度、残余应力、元素含量等的影响。结果表明:喷丸强化后,试样表面留有大量弹坑,产生明显塑性变形;表面粗糙度增大,算术平均粗糙度为1.33μm;硬度显著增大,最表层硬度由喷丸前的HV476增加至HV497,硬化层深度约150μm;试样表层的残余压应力值由375MPa增加至475MPa,最大残余压应力值约518MPa,位于距表面50μm深度处,喷丸形成的残余压应力层深度约为134μm;喷丸后试样中C、Si、Cr等各元素的质量分数均略有增加。喷丸在一定程度上改善了23Co14Ni12Cr3Mo钢材料的表面性能,有利于提高其疲劳抗力和耐腐蚀性。

简介：为确定热加工性能的最佳条件，在温度350~500°C、应变率0.0005~0.5s-1下研究Al6061/Al2O3纳米复合材料的热压缩行为。采用双曲正弦函数得到材料热压缩测试活化能为285kJ/mol。用动态材料模型和相应的加工图，确定了温度450°C、应变速率0.0005s-1和温度500°C、应变速率0.0005~0.5s-1为Al6061/Al2O3材料的热加工性能安全区，最大功率损耗率为38%。由于材料大变形，在温度400°C和应变速率0.5s-1下得到了被伸长和扭结晶粒。

简介：1综述3月份的铂族金属市场备受关注，供应局势风起云涌。南非铂矿山继续罢工，已经持续两个多月，造成超过100亿南非兰特损失。劳资双方差距太大，政府协调的谈判进展缓慢，调解机构甚至受到矿山协会的指责。克里米亚独立并入俄罗斯联盟的公投获得通过，欧美国家制定对俄罗斯经济制裁计划。

简介：文章摘要：2011年以来（1-9月）国际大宗商品市场中黄金一枝独秀，成为表现最好、涨幅最大的大宗商品品种，经济危机中黄金的金融属性进一步得到彰显；当前全球黄金市场基本面变化不大，黄金供应瓶颈依然存在，而黄金需求维持稳定；只不过全球供应需求重心开始逐步转移，印度中国黄金进口大增需求占全球黄金需求的近一半；

简介：在H2SO4-Fe2（SO4）3体系中研究载金黄铁矿的浸出动力学,探讨反应温度、Fe3＋浓度、硫酸浓度、搅拌速度等对黄铁矿浸出的影响规律。结果表明：在H2SO4-Fe2（SO4）3体系中,在30~75°C下黄铁矿浸出过程主要受化学反应控制Fe3＋浓度与黄铁矿的浸出呈正相关,通过Arrhenius经验公式求得浸出表观活化能为51.39kJ/mol。EDS与XPS分析结果表明：黄铁矿氧化过程中硫的氧化经一系列中间形态,最终被氧化成硫酸根,并伴有部分元素硫生成,符合硫代硫酸根氧化路径机理。

简介：采用分子动力学方法对Mg7Zn3合金快速凝固过程进行计算机模拟，研究玻璃转变过程局域结构与动力学之间的关联。结果表明：以Mg原子为中心的FK多面体和以Zn原子为中心的二十面体局域结构，对Mg7Zn3金属玻璃的形成起关键性作用。Mg（Zn）原子的扩散系数在熔点附近开始偏离Arrhenius关系，而满足幂指数规律。根据均方位移、非相干中间散射函数和非Gauss函数等时间相关函数，发现：随着温度的降低，β驰豫越来越显著，α弛豫时间以VFT指数规律迅速增加；而且半径较小的Zn原子比Mg原子呈现较快的弛豫动力学行为。另外，部分短程有序局域原子结构具有较慢的动力学行为，对β驰豫中笼子效应起主导作用；并随着其数目的大量出现，体系扩散系数开始偏离Arrhenius关系，玻璃形成过程微观结构转变温度TgStr与动力学转变温度Tc非常接近。

简介：研究VC/Cr3C2对Ti(C,N)基金属陶瓷微观组织和力学性能的影响。利用光学显微镜、X射线衍射仪和扫描电镜结合能谱仪研究微观组织。测试横向断裂强度、硬度和断裂韧性等力学性能。结果表明:微观组织中存在"黑芯-灰壳"和"白芯-灰壳"结构;由于添加VC/Cr3C2,硬质相晶粒变细,添加0.75VC/0.25Cr3C2的金属陶瓷晶粒细化最明显;黑芯随着VC添加量的增加而变细,壳随着Cr3C2添加量的减少而变厚;孔隙率随着VC/Cr3C2中VC的量增加而增大;横向断裂强度和硬度均升高,并且均在添加0.25VC/0.75Cr3C2时达到最大值;按适当的VC和Cr3C2添加量比例添加VC/Cr3C2可以有效地使断裂韧性升高,并在添加0.5VC/0.5Cr3C2时取得最大值。