简介:Inthispaper,themicrostructureandhardnessofHG980Dheat-affectedzone(HAZ)atdifferentcoolingratet8/3werestudied,theimplantcriticalfracturestressunderthreediffusiblehydrogenconditionsweremeasured,andthehydrogen-inducedcracking(HIC)fractographofsteelHG980Dwereanalyzed.TheexperimentalresultsshowthatmartensiteexistsinHAZofHG980Dtillt8/3≥150s,thehardenquenchingtendencyofHG980Disgreater;Theimplantcriticalfracturestressisrelatedtodiffusiblehydrogencontentsignificantly,atlowhydrogenlevel,highrestraintstressisneededtonucleateHIC,thefractographismainlymicrovoidcoalescence,butathighhydrogenlevel,onlysmallrestraintstresscancauseHICoccurrence,thefractographismainlyquasicleavage.Itisveryimportanttochooseultra-lowhydrogenweldingconsumabletoweldsteelHG980Dtopreventhydrogen-inducedcracking.
简介:介绍一种金属/合金的生产方法,用于恒电流和恒电位条件下由混合硫化物(Cu2S,NiS)生产Cu-Ni合金,称为直接电化学还原(DER)。研究槽电压和槽电流等工艺参数对还原得到的化合物组成的影响,以生产工业所需的CuNi10,CuNi20和CuNi30等合金。在1200°C下采用循环伏安法(CV)考察Cu2S和NiS在CaCl2熔体中的电化学行为。根据CV研究结果,Cu2S的阴极还原是一步完成的,即Cu2S?Cu;NiS的阴极还原则分两步进行,即NiS?Ni3S2?Ni。恒电流研究表明,在10A电流下电解15min,可制备出最高硫含量为320×10-6的高纯CuNi10合金。扫描电子显微镜以及能量色散X射线能谱和光学发射光谱(OES)测试结果表明,在2.5V电压下直接电化学还原15min,可制备出杂质含量低(即硫含量小于60×10-6)的所选成分的Cu-Ni合金。
简介:Microstructuresandmechanicalpropertiesoftransientliquidphase(TLP)bondedmagnesiummetalmatrixcomposite(MMC)jointsusingcopperinterlayerhavebeeninvestigated.Withanincreaseofbondingtimesfrom5minto50minatbondingtemperatureof510℃,theaverageconcentrationofcopperinthebondedzonedecreased,themicrostructureinthezonechangedfromCu,α-MgandCuMg2toα-Mg,CuMg2andTiC,andmechanicalpropertiesofthejointincreased.Theshearstrengthofthejointbondedat510℃for50minreached64MPaduetothemetallurgicalbondingofthejointandimprovingitshomogeneityofcompositionandmicrostructure.ItisfavorabletoincreasethebondingtimeforimprovingmechanicalpropertiesofTLPbondedmagnesiumMMCjoint.
简介:ThesusceptibilityofweldedjointfortheX65pipelinesteeltoH2Sstresscorrosioncracking(SCC)isinvestigated.SCCtestsonthesteelarecarriedoutintheenvironmentbasedonNACETM-01-77solutionwithsaturatedgaseousH2S.Thethresholdstressintensityfactorandcrackpropagationvelocityarecalculatedaccordingtowedge-openingloading(WOL)specimens.Thethree-dimensionalelastic-plasticfiniteelementanalysisofWOLspecimensisperformedbyusingtheFEMprogrammingpackageANSYS.Stressfieldandconcentrationofhydrogendistributionpropertyaheadofthecracktipareobtained.ThispapersurveyedthemicrostructureofweldedjointandstudiedonthemechanicalpropertiesofX65pipelinesteel.Itprovidesexperimentalbasisforstudyingstresscorrosion.Theresultsofnumericalanalysisareconsistentwithconclusionsofstresscorrosiontest.
简介:作为驱动第四次工业革命的重要力量,3D打印正被提升到国家战略层面,成为传统制造产业关注的焦点。据悉,为加快推动3D打印制造技术的研发和产业化,国家相关部门制定了推动3D打印发展的国家政策及具体推动措施。国家对3D打印的支持力度的加大,我国3D打印产业将迎来新一轮发展机遇。智能再制造政策激励3D打印产业发展2017年11月9日,工信部发布《高端智能再制造行动计划(2018-2020年)》,其中明确提到加快增材制造、特种材料、智能加工、无损检测等再制造关键共性技术创
简介:基于d-电子合金设计理论和JMatPro软件,运用正交试验,设计了具有较低弹性模量和较高强度且含有无毒元素Nb、Mo、Zr和Sn的新型生物医用∥钛合金Ti-35Nb-4Sn-6Mo-9Zr,并对该合金的显微组织和力学性能进行分析。结果表明,Ti-35Nb-4Sn-6Mo-9Zr合金在800。C下固溶处理后,由单一的β等轴晶构成。与Ti-6Al-4V相比,该合金具有较优越的力学性能:E=65GPa,σb=834MPa,σ0.2=802MPa,6=11%,有望成为新型种植材料。该方法可以有效地降低实验次数,并得到理想的实验结果。