简介:AseriesofCe-Fe-Zr-O(x)/MgO(xdenotesthemassfractionofCe-Fe-Zr-O,x=10%,15%,20%,25%,30%)complexoxideoxygencarriersforselectiveoxidationofmethanetosynthesisgaswerepreparedbytheco-precipitationmethod.ThecatalystswerecharacterizedbymeansofX-raydiffractionandH2-TPR.TheXRDmeasurementsshowedthatMgFeO4particleswereformedandFe2O3particleswelldispersedontheoxygencarriers.Thereactionsbetweenmethanedilutedbyargon(10%CH4)andoxygencarrierswereinvestigated.SuitablecontentofCeO2/Fe2O3/ZrO2mixedoxidescouldpromotethereactionbetweenmethaneandoxygencarriers.Therearemainlytwokindsofoxygenofcarriers:surfacelatticeoxygenwhichhadhigheractivitybutlowerselectivity,andbulklatticeoxygenwhichhadloweractivitybuthigherselectivity.Amongallthecatalysts,Ce-Fe-Zr-O(20%)/MgOexhibitedthebestcatalyticperformance.Theconversionofthemethanewasabove56%,andtheselectivityoftheH2andCOwerebothabove93%,theratioofH2/COwasstableandapproachedto2foralongtime.
简介:InordertoimprovethehydrogenationanddehydrogenationperformancesoftheMg2Ni-typealloys,MgwaspartiallysubstitutedbyLainthealloy,andmeltspinningtechnologywasusedforthepreparationoftheMg20-xLaxNi10(x=0,2,4,6)hydrogenstoragealloys.ThestructuresofthealloyswerestudiedbyX-raydiffraction(XRD),scanningelectronmicroscopy(SEM)andhigh-resolutiontransmissionelectronmicroscopy(HRTEM).Itwasfoundthatnoamorphousphaseformedintheas-spunLa-freealloy,buttheas-spunalloyscontainingLaheldamajoramorphousphase.WhenLacontentx≤2,themajorphaseintheas-castalloyswasMg2Niphase,butwithfurtherincreaseofLacontent,themajorphaseoftheas-castalloyschangedintoLaNi5+LaMg3phase.Thermalstabilityoftheas-spunalloyswasstudiedbydifferentialscanningcalorimetry(DSC),showingthatspinningratewasanegligiblefactoronthecrystallizationtemperatureoftheamorphousphase.Thehydrogenabsorptionanddesorptionkineticsoftheas-castandas-spunalloysweremeasuredusinganautomaticallycontrolledSievertsapparatus,confirmingthatthehydrogenabsorptionanddesorptioncapacitiesandkineticsoftheas-castalloysclearlyincreasedwithrisingLacontent.ForLacontentx=2,theas-spunalloydisplayedoptimalhydrogendesorptionkineticsat200°C.
简介:EffectofLa-richrareearthoneutecticmicrostructureinA1-2%Fealloywasstudied.WhentheadditionofREissmall,a-A1phaseisintheformofcellulardendrite.WiththeincreaseoftheadditionofRE,thenucleationandgrowthofa-A1dendritearesuppressed,andeutecticAl3Fephaseisrefined.WhentheadditionofREgetsto0.6%(massfrac-tion),thesizeofeutecticAl3Feincreases.Inaddi-tion,mechanismoftheeffectofmixedREoneutecticmorphologyofA1-2%Fealloyisexplored.
简介:EffectofMnsubstitutionforFeincubicLavesZr0.1Tb0.9(Fe1-xMnx)2andY0.1Tb0.9(Fe1-xMnx)2com-poundsispresented.Similarresultsinbothsystemsareobtained:ThestructureandthemagnetismofTbFe2arebothinfluencedslightlybyasmallamountofYorZrsubstitutionforTb;Withincreasingxvalue,thelatticeconstantincreasesmonotonously;theCurietemperaturedecreaseslinearly;whilesaturationmagnetizationincreaseslinearly.ForthesmallamountofMnsubstitutionforFeinbothsystems,magnetostrictionissignificantlylargerthanthatinthepureironalloys.Thelargestmagnetostrictionof|γ‖-|γ|=2200×10-6atmagneticfieldof2×107/4πA/misobtainedforY0.1Tb0.9(Fe0.95Mn0.052.