简介：本文采用真空钎焊工艺对1Cr18Ni9Ti不锈钢进行了焊接,焊后通过扫描电镜、电子探针扫描、XRD等分析测试手段对试样进行分析研究。研究结果表明:试样表面生成了碳化物,为TiC和Ti8C5;表面碳化物的生成过程是在真空高温环境下,Ti元素与环管中向外扩散的C发生固相扩散反应生成TiC,过量的Ti再与TiC反应生成Ti8C5。

简介：Mg–9Li–3Al–1.6Yalloyswerepreparedthroughmixturemethod.Themicrostructure,mechanicalproperties,andcorrosionresistanceoftheas-castandasextrudedalloyswerestudiedbyopticalmicroscopy（OM）,scanningelectronicmicroscopy（SEM）,X-raydiffraction（XRD）,mechanicalpropertiestesting,andelectrochemicalmeasurement.Theas-castMg–9Li–3Al–1.6Yalloywiththeaveragegrainsizeof325lmiscomposedofb-Limatrix,blocka-Mg,andgranuleAl2Yphases.Afterextrusion,thegrainsizeoftheas-castalloyisobviouslyrefinedandreachesto75lm;thestrengthandelongationoftheextrudedalloyareenhancedby17.20%and49.45%,respectively,owingtotheirfinemicrostructureandreductionofcastingdefects.Theas-extrudedalloyshowsbettercorrosionresistancecomparedtotheas-castone,whichmayberelatedtothelowstoredenergyanddislocationdensityintheextrudedalloy,alsothehomogenizationtreatmentbeforeextrusion.