简介：ActiveFe-andMn-loadedMCM-41(Fe–Mn/MCM-41),whichwassynthesizedviaahydrothermalreactionfollowedbyimpregnation,isusedintheheterogeneousFentonreactiontodegrademethylorange(MO)inaqueoussolution.ThesynthesizedsampleswerecharacterizedbyX-raydiffraction,scanningelectronmicroscopy,transmissionelectronmicroscopy,N2adsorption–desorptionisothermanalysis,Fouriertransforminfraredspectroscopy,andX-rayphotoelectronspectroscopy.ComparedwithFe/MCM-41andMn/MCM-41,Fe–Mn/MCM-41showedhigheractivityforMOdegradationandmineralization.Effectsofvariousoperatingparameters,suchaspH,Mncontent,andH2O2dosage,onthedegradationprocessweresubsequentlyinvestigated.ResultsofexperimentsontheeffectofradicalscavengersrevealedthatthedegradationofMOcouldbeattributedtooxidationbyHO·.ThesynergyofFeandMnspeciesintheFentonoxidationprocesswasalsoexplained.

简介：采用脉冲激光沉积方法，以烧结的Fe3O4为靶材，在STO（100）基底上制备了Fe3O4（100）薄膜。XRD和AFM显示薄膜为纯相外延单晶薄膜、表面较平整。对薄膜的磁电阻进行测量，薄膜为负磁电阻，且在Verwey转变温度（约120K）时磁电阻最大。霍尔效应测量得到薄膜中栽流子浓度随着温度的降低而减小，In（n）与I／T基本呈线性关系，符合半导体热激活模型，迁移率随着温度的降低而减小，说明在薄膜内存在大量电离杂质中心。薄膜磁滞回线中较高的饱和磁化场。说明薄膜中APBs密度较低。

简介：采用IBS法在锡青铜衬底上溅射沉积Sm-Fe非晶态超磁致伸缩薄膜，研究衬底的表面状态和薄膜热处理对Sm-Fe薄膜磁致伸缩性能的影响。实验结果表明，锡青铜衬底状态对Sm-Fe超磁致伸缩薄膜磁伸性能有很大影响。样品经过200℃真空热处理后，100mT内dλ/dH值从制备态Sm-Fe薄膜的0．71×10^-3T^-1提高到2．48×10．3T^-1，薄膜低场磁敏性得到显著提高。

简介：通过制备4种不同锰镍比的TWIP合金铸铁,研究了锰镍比对Fe-Mn-Ni系TWIP合金铸铁组织和力学性能的影响。试验结果表明：随着锰镍比从3∶2、2∶1、3∶1和4∶1逐渐增加,铸铁铸态组织中的碳化物含量增加。在1050℃保温10h后进行水淬,就能使碳化物分解,获得单相奥氏体基体组织。经过热处理后,锰镍比为3∶2的TWIP合金铸铁力学性能最佳,其抗拉强度为885MPa,伸长率为29.7%。

简介：通过改变加热温度和保温时间,研究不同热处理工艺对Fe-16Mn-3.5C-3Si-3Cu高锰TWIP合金铸铁组织的影响,对试样进行物相分析和金相组织观察。实验结果表明：随着加热温度和保温时间的增加,组织中退火孪晶的数量增加,孪晶发育趋于完善。热处理后其室温组织为单一奥氏体;热处理的合金铸铁拉伸变形后,产生大量形变孪晶,其变形后的基体仍然保持单一奥氏体组织,未发生马氏体相变,发生了完全的TWIP效应。