简介：CeO2andCuOx-CeO2supportedpotassiumcatalystsweresynthesizedbywetnessimpregnationmethod.ThecatalystswerecharacterizedbyBET,NO-TPO,NOx-TPDandsoot-TPOmeasurements.Bythedecorationofpotassiumandcopper,themaximumsootcombustiontemperatureoftheceria-basedcatalystdecreasedto338and379°CinthepresenceandabsenceofNOunderaloosecontactmode,re-spectively.ThepronouncedlyenhancedNOoxidationabilitybycopperintroductionandNOxstoragecapacitybypotassiummodif...

简介：ThedopedZnOnanorodsasaphotocatalystwithdifferentEucontentswerepreparedbymicrowaveassistedmethodandtheywerecharacterizedbymeansofX-raydiffraction(XRD),energy-dispersiveX-rayspectroscopy(EDS),UV-Visspectroscopy,surfaceareaBrunauer-Emmett-Teller(BET),X-rayphotoelectronspectroscopy(XPS),scanningelectronmicroscopy(SEM)andtransmissionelectronmicroscopy(TEM).TheaveragecrystallitesizeandbandgapenergyofEu-dopedZnOwerevariedwiththeEucontent.TheXRDpatternofEu-dopedZnOindicatedhexagonalcrystalstructurewithanaveragecrystallitesizeof25nm.ThepresenceofeuropiumwithtrivalentstateanditsdopingsuccessfullyintothecrystallatticeofZnOmatrixwereconfirmedbyXPStechnique.ThephotocatalyticactivityofEu-dopedZnOnanorodswasevaluatedformethylorangedegradation.Thephotocatalyticexperimentsshowed～91%degradationofmethylorangeover0.2mol.%EudopedZnOsamplewithin3hunderUVlight(365nm).

简介：有TbCu7结构的SmCo6.6Nb0.4nanoflakes被帮助表面活化剂的高精力球milling(SA-HEBM)成功地作为milling媒介与heptane和油的酸准备。微观结构，水晶结构和磁性被分别地扫描电子显微镜学，X光检查衍射，和颤动的样品磁强计学习。nanoflakes的结晶的排列和coercivity系统地被调查的c轴上的球milling时间的效果。研究证明nanoflakes有100nm的平均厚度，1m的一条平均直径，与象100一样高的方面比率。作为时间从2～8h增加了的球milling，思考达到顶点紧张比率我(002)/I(101)显示了SmCo6.6Nb0.4阶段的c轴水晶质地的度，增加了第一，在4h到达了一座山峰，然后减少。同时，nanoflakes的coercivity也增加了第一，为4h在13.86kOe到达了一座山峰，然后减少。

简介：混合氧化物(Ce0.6Zr0.4O2)由帮助微波的加热一起沉淀准备了的CeO2-ZrO2被用作支持经由早期湿的受精的方法与各种各样的CuO内容(0wt.%15wt.%)准备一系列CuO/Ce0.6Zr0.4O2催化剂。获得的CuO/Ce0.6Zr0.4O2样品被N2吸附，XRD，拉曼，TEM和H2-TPR技术，和他们的催化活动描绘因为公司氧化被调查。结果证明CuO/Ce0.6Zr0.4O2催化剂的活动被CuO的内容强烈影响，并且有10wt.%CuO的催化剂在公司氧化展出了最好的催化活动，它能在催化剂被归因于CuO，和高氧空缺集中的高分散和reducibility。