简介:Inthisstudy,theformabilityoftransformation-inducedplasticity(TRIP)steelisstudiedduringdeep-drawingprocesseswithpreforming.Theeffectsofpreformingontheminimumthicknessofcanareinvestigatedwithaconstitutivemodelaccompanyingstrain-inducedmartensitetransformationinprestraincondition.TheconstitutivemodelhasbeenimplementedintoABAQUS/UMATforanalysisofTRIPsteel-formingprocesses.TheresultsshowthatpreformingslightlyinfluencesthethicknessuniformityofTRIPsteel...
简介:Thephasetransformationcharacteristicsofahigh-strengthTRIP-aidedmultiphasecold-rolledsteelduringcontinuousheatingatdifferentcoolingrateswerestudiedbymeansofdilatometry,andthecriticaltemperatureswerealsodetermined.Thesampleswerefullyaustenitizedat1050℃andthencooledatdifferentcoolingratesrangingfrom0.5℃/sto100℃/s.Thecontinuouscoolingtransformation(CCT)curveswereobtainedfortheexperimentalsteel.Theexperimentalresultsshowedthatahighcoolingratedepressedtheformationofferriteandpearliteandpromotedtheformationofbainiteandmartensite,leadingtoahigherhardness.Alargeamountofmartensiteinhigh-strengthTRIP-aidedmultiphasecold-rolledsteelcanbeobtainedatcoolingratesinexcessof50℃/s.Theexperimentalresultsprovideguidelinesforcoolingcontrolandheattreatmentinrealsteelproduction.
简介:Thetransformationinducedplasticity(TRIP)steelseffectoccursbecauseofthemartensitictransformationofretainedausteniteduringplasticdeformation,anditprovidesthesteelwithexcellentstrengthandductility.Whileweldingremainsavitalpartofautobodymanufacturing,theweldabilityofTRIPsteelsisproblematic,andthispreventsitsadoptionformanyapplicationsintheautomotiveindustry.Thispresentworkstudiestheeffectsofweldingandpost-weldheattreatmentonthemicrostructureof...