摘要
Themicrostructuresofas-castandas-solutionMg–12Gd–2Er–1Zn–0.6Zralloyswereinvestigatedbyopticalmicroscopy（OM）,scanningelectronmicroscopy（SEM）,transmissionelectronmicroscopy（TEM）,highresolutiontransmissionelectronmicroscopy（HRTEM）X-raydiffraction（XRD）andselected-areaelectrondiffraction（SAED）inthepresentinvestigation.TheresultsshowthattheprimaryeutecticphaseMg5（Gd,Er,Zn）andsomeflocculentfeaturesarefoundintheas-castalloy;theSAEDpatternindicatesthattheseflocculentfeaturesarethedenseareasofstackingfaults.The14H-LPSOstructureprecipitatesinthetemperaturerangeof673–793K,andthevolumefractionof14H-LPSOstructureincreaseswiththeextensionofheatingtime;however,thereisnoprecipitationof14H-LPSOstructurewhenthetemperaturereachesupto803K.Inaddition,theMg5（Gd,Er,Zn）phasedissolvesgraduallyalongwiththeprecipitationof14H-LPSOstructure.