摘要
Fe2O3/activecarbon(Fe2O3/AC)nanocompositeswerereadilyfabricatedbypyrolyzingFe3+impregnatedactivecarboninanitrogenatmosphere.Theas-preparedcompositeswerestudiedbyX-raypowderdiffraction(XRD),X-rayphotoelectronspectroscopy(XPS)andtransmissionelectronmicroscopy(TEM).Thecapacitivepropertyofthecompositeswasinvestigatedbycyclicvoltammetry(CV)andgalvanostaticcharge-dischargetest.Physicalcharacterizationsshowthattheγ-Fe2O3finegrainsdispersedintheACwell,withameansizeof21.24nm.Electrochemicaltestsin6mol/LKOHsolutionsindicatethattheas-preparednanocompositesexhibitedimprovedcapacitiveproperties.Thespecificcapacitance(SC)ofFe2O3/ACnanocompositeswasupto188.4F/gthatwasderivedfrombothelectrochemicaldouble-layercapacitanceandpseudo-capacitance,whichwas78%largerthanthatofpristineAC.AsymmetriccapacitorwithFe2O3/ACnanocompositesaselectrodeshowedanexcellentcyclingstability.TheSCwasonlyreducedbyafactorof9.2%after2000cyclesatacurrentdensityof1A/g.
出版日期
2012年05月15日(中国期刊网平台首次上网日期,不代表论文的发表时间)