简介:Pt(Ⅱ)andPd(Ⅱ)complexeswith2',3',4',5,7-pentahydroxy-flavoneweresynthesizedandcharacterizedbyelementalanalysis,molarconductance,IR,1HNMR,TG-DTA,UV-Visspectroscopictechniques,andfluorescenceanalysis.Thescavengingeffectonthesuperoxideradical(O-2)andtheinhibitoryeffectonlipidperoxideswerealsoinvestigated.Boththeligandandthecomplexesexhibitscavengingeffectonsuperoxideradicals,andtheeffectofthecomplexesisgreaterthanthatoftheligand.ThePt(Ⅱ)complexexhibitsthestrongestscavengingefficiency.BothPt(Ⅱ)andPd(Ⅱ)complexeshavetheinhibitoryeffectonlipidperoxides,andtheeffectofthecomplexesisgreaterthanthatoftheligand,butthePt(Ⅱ)complexhasahigheffectofpromotinglipidperoxides.
简介:通过水热法成功合成Co3O4/CuO复合物,并探索十六烷基三甲基溴化铵(CTAB)和聚乙烯吡咯烷酮(PVP)对其形貌和性能的影响。用X射线衍射仪(XRD)、扫描电子显微镜(SEM)、透射电子显微镜(TEM)和氮气吸附-脱附测试表征其微观结构和表面形貌。采用循环伏安、恒流充放电和交流阻抗测试等方法研究样品的电化学性能。结果表明,多孔Co3O4/CuO-CTAB纳米片具有最好的电化学性能,在电流密度1A/g下的比容量达398F/g,而在10A/g时其比容量仍能保持90%。此外,该复合物具有很好的循环稳定性,在2000次循环后容量几乎没有衰减。
简介:通过湿法球磨制备CoFe2O4-BaTiO3颗粒复合材料,研究材料成分和调制频率与电磁效应的关系。结果表明:电磁效应系数随着调制频率由400Hz增加到1000Hz而增加。由于CoFe2O4的电导率在400-1000Hz范围内对频率敏感,电磁效应的曲线特性而发生改变。在烧结过程中形成第三相Ba2Fe2O5,从而导致电磁效应的下降。
简介:研究了AlTi5B1晶粒细化和冷却速率对AlSi7Cu3Mg二次合金显微组织和力学性能的影响。采用阶梯铸模在不同冷却速率下制备添加晶粒细化剂的合金,并利用金相和图像分析技术定量研究了合金的宏观组织和显微组织。研究结果表明,添加AlTi5B1后,整个铸件具有细小均匀的晶粒组织,且在慢速凝固区域效果更显著。当冷却速率增加时,少量细化剂就可使铸件获得细小均匀组织。另外,原材料中的Ti和B以杂质的形式存在,不足以形成有效的晶粒细化效果。利用阶梯铸造法的研究结果研究了重力半固模铸造16V汽油发动机气缸盖。Weibull统计结果表明,晶粒细化改善了合金的塑形变形行为,提高了铸件的可靠性。
简介:Mg–9Li–3Al–1.6Yalloyswerepreparedthroughmixturemethod.Themicrostructure,mechanicalproperties,andcorrosionresistanceoftheas-castandasextrudedalloyswerestudiedbyopticalmicroscopy(OM),scanningelectronicmicroscopy(SEM),X-raydiffraction(XRD),mechanicalpropertiestesting,andelectrochemicalmeasurement.Theas-castMg–9Li–3Al–1.6Yalloywiththeaveragegrainsizeof325lmiscomposedofb-Limatrix,blocka-Mg,andgranuleAl2Yphases.Afterextrusion,thegrainsizeoftheas-castalloyisobviouslyrefinedandreachesto75lm;thestrengthandelongationoftheextrudedalloyareenhancedby17.20%and49.45%,respectively,owingtotheirfinemicrostructureandreductionofcastingdefects.Theas-extrudedalloyshowsbettercorrosionresistancecomparedtotheas-castone,whichmayberelatedtothelowstoredenergyanddislocationdensityintheextrudedalloy,alsothehomogenizationtreatmentbeforeextrusion.
简介:ThemicrostructuresandcrystallizationbehaviorofTi–47at%Ni–3at%Feshapememoryalloywireundertheconditionofseverecolddrawingatroomtemperatureanddifferentpost-deformationannealingprocesseswereintensivelyinvestigatedusingtransmissionelectronmicroscope(TEM)anddifferentialscanningcalorimetry(DSC).ItisindicatedthattheamorphousphaseisdominantintheTi50Ni47Fe3wireafterthecolddrawingof78%arealreduction.Thecriticaltemperatureforrecrystalizationisdeterminedatabout300°C.Theaveragegrainsizegrowsfrom7upto125nmwhenannealingtemperaturerisesfrom300to500°C.Post-deformationannealingprocessexertssignificantinfluenceonthecrystallizationtemperaturewhichclimbsupwiththeincreaseofannealingtemperature.
简介:Au/-Al2O3催化剂被免职降水方法为低集中白酒溪流(甲醇,乙醇,iso-propanol和n-propanol)的催化燃烧作好准备。催化剂被X光检查光电子描绘光谱学(XPS),X光检查diffractometry(XRD)和精力散X光检查微分析(版本)技术。XPS结果证明仅仅催化剂的表面上有Au0。XRD模式证明Au高度大概在-Al2O3上被驱散。为有2.0g/m3的集中的甲醇,乙醇,iso-propanol和n-propanol的完全的变换的温度是60,155,170和137?,分别地但是他们完全在60,220,260和217点被使矿物化进CO2和H2O吗?分别地在优化催化剂上。催化剂的活动在130h是稳定的。为催化甲醇消除的动力学跟随了伪--首先订表示为r=0.6528c0+0.084的反应2。明显的激活精力的价值是在反应温度的范围的54.7kJ/mol。
简介:TheeffectofyttriaonthesolidreactionmechanismofaCaHPO4·2H2O+CaCO3systematdifferenttemperatureswasexperimentallystud-ied.Thesampleswithandwithoutyttriaweresubjectedtothermogravimetric/differentialscanningcalorimetrymeasurement.ThesampleswereheattreatedatthetemperaturescorrespondingtothepeaksontheDSCspectra,andtheresultedphasecompositionswereidentifiedbyX-raydiffraction.Thetransformationmechanismwasdeducedbycomparingthephasesobtainedatdifferenttemperatures.Theresultsshowthatthetransformationsatbelow1073Karenotaffectedbyyttria,butallthoseatabove1073Karecompletelyaltered.Theformationtem-peratureofhydroxyapatitedecreasesby134K,andthedecompositiontemperatureincreasesby38K.ThepolymorphoustransformationofCa3(PO4)2fromβphasetoαphaseincreasesby47K.Thethermodynamicpropertiesofthetransformationsatabove1073Karealsomodi-fiedbytheadditionofyttria;thatis,theendothermalpeaksaresubstitutedbyexothermalpeaks.